NON-BLOOMING FLAME RETARDANT
HIGH DENSITY POLYETHYLENE
FARALLOY PE-106
FARALLOY PE-106 is an extrusion grade, UV resistant, non-blooming flame retardant high density polyethylene formulated to resist ignition as defined by Underwriters’ Laboratories 94V-0 test protocol.
| Physical Property |
ASTM Method |
Metric Value |
English Value |
|
Melt Index @ 1900C @ 21.6 Kg |
D1238 |
24 g/10 min. |
|
| Specific Gravity |
D792 |
1.29 g/cc |
|
| Tensile Strength |
D638 |
26.9 MPa |
3,900 psi |
|
Elongation at Break |
D638 |
100% |
100% |
|
Flexural Modulus |
D790 |
1034 MPa |
150,000 psi |
|
Flexural Strength |
D790 |
27.6 MPa |
4,000 psi |
|
Notched Izod |
D256 |
224 J/m |
3.5 ftlb/in |
|
Heat Deflection Temperature 66 psi |
D648 |
850C Annealed |
1850F Annealed |
|
Flammability |
ICC Laboratory Test in accordance with UL-94V Test Procedure |
V-0 @ 1.5mm |
V-0 @ 0.0625 in. |
Caution: This product contains a special FR component which may lose its effectiveness after repeated extrusions. Regrind content of blends should be kept to a minimum and the fire retardancy of resulting sheet tested prior to sale.
Note: These data are typical properties and are not to be used for establishing minimum material specifications. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Industries Incorporated for specific data to meet your design criteria.