35% TALC FILLED
HIGH MOLECULAR WEIGHT POLYETHYLENE
FARALLOY PE-204
FARALLOY PE-204 is a talc filled extrusion compound designed to increase the heat deflection properties while maintaining a high impact strength.
| Physical Property |
ASTM Method |
Metric Value |
English Value |
|
Melt Index @ 1900C @ 21.6 Kg |
D1238 |
7 g/10 min. |
|
| Specific Gravity |
D792 |
1.13 g/cc |
|
| Tensile Strength |
D638 |
27.6 MPa |
4,000 psi |
|
Elongation at Break |
D638 |
30% |
30% |
|
Notched Izod |
D256 |
53.4 J/m |
1 ftlb/in |
|
Heat Deflection Temperature 66 psi |
D648 Annealed Unannealed |
1070C 860C |
2250F 1870F |
Note: These data are typical properties and are not to be used for establishing minimum material specifications. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Chemical Corporation for specific data to meet your design criteria.