SEMI-CONDUCTIVE BLACK POLYETHYLENE FARALLOYÒ PE-410 |
FARALLOY PE-410 is a rotomolding grade black semi-conductive polyethylene available as a rotomoldable powder. As a pellet, this formulation would be suitable for extrusion and injection molding processes.
|
Physical Property |
Test Method | Metric Value | English Value |
| Melt Index @ 190° C @ 2.16 Kg | ASTM D1238 | 4.1 g/10 min. | |
| Specific Gravity | ASTM D792 | 0.961 | |
| Tensile Strength | ASTM D638 | 20.7 MPa | |
| Elongation at Break | ASTM D638 | 120% | 120% |
| Flexural Modulus | ASTM D790 | 558 MPa | 81,000 psi |
| Flexural Strength | ASTM D790 | 17.2 MPa | 2,500 psi |
| Notched Izod | ASTM D256 | 133 J/m | 2.5 ft lb/in |
| Heat Deflection Temperature 66 psi | ASTM D648 | 75° C Annealed | 167° F Annealed |
| Surface Resistivity | ICC Lab. Test | 105 Ohms/Sq. |
NOTE: These data are typical properties and are not to be used for establishing material minimums. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Chemical Corporation for specific data to meet your design criteria.