FIBROUS MINERAL REINFORCED
LINEAR LOW DENSITY POLYETHYLENE
FARALLOY PE-425 (0899-76)
PRELIMINARY DATASHEET
FARALLOY PE-425 (0899-76) is a rotational molding grade linear low density polyethylene that is modified with a high aspect ratio mineral filler to increase stiffness and dimensional stability while reducing mold shrinkage.
| Physical Property |
ASTM Method |
Metric Value |
English Value |
|
Melt Index @ 1900C @ 2.16 Kg |
D1238 |
5.5 g/10 min. |
|
| Specific Gravity |
D792 |
1.09 g/cc |
|
| Tensile Strength |
D638 |
15.8 MPa |
2,300 psi |
|
Elongation at Break |
D638 |
330% |
330% |
|
Flexural Modulus (LLDPE) |
D790 |
803 MPa (455MPa) |
116,500 psi (66,000 psi) |
|
Flexural Strength |
D790 |
19.3 MPa |
2,800 psi |
|
Notched Izod |
D256 |
107 J/m |
2.0 ftlb/in |
|
Heat Deflection Temp. 66 psi (LLDPE) |
D648 |
67 0C (520C) |
152 0F (1260F) |
|
Mold Shrink (LLDPE) |
D955 |
|
0.015 in/in (0.027 in/in) |
Note: These data are typical properties and are not to be used for establishing minimum material specifications. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Industries Incorporated for specific data to meet your design criteria.