FLAME RETARDANT
POLYPROPYLENE
FARALLOY PP-114
FARALLOY PP-114 is an extrusion grade polypropylene, economically formulated to resist ignition as defined by Underwriters’ Laboratories 94V-2 test protocol. It is intended for use in non-aesthetic application due to a slight surface bloom.
| Physical Property |
ASTM Method |
Metric Value |
English Value |
|
Melt Index @ 2300C @ 2.16 Kg |
D1238 |
1.4 g/10 min. |
|
| Specific Gravity |
D792 |
0.93 g/cc |
|
| Tensile Strength |
D638 |
34.5 MPa |
5,000 psi |
|
Elongation at Break |
D638 |
300% |
300% |
|
Flexural Modulus |
D790 |
1,400 MPa |
203,000 psi |
|
Flexural Strength |
D790 |
42.8 MPa |
6,200 psi |
|
Heat Deflection Temperature 66 psi |
D648 |
980C |
2080F |
|
Flammability |
ICC Laboratory Test in accordance with UL-94V-2 test procedures |
V-2 @ 3.0mm |
V-2 @ 0.125 in. |
Note: These data are typical properties and are not to be used for establishing minimum material specifications. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Industries Incorporated for specific data to meet your design criteria.