FLAME RETARDANT
POLYPROPYLENE
FARALLOY PP-135
FARALLOY PP-135 is a very tough extrusion grade flame retardant polypropylene formulated to resist ignition as defined by Underwriters’ Laboratories 94V test protocol. This material contains no talc, which is normally used to prevent olefin products from dripping during flame testing at the expense of impact resistance (toughness).
|
Physical Property |
ASTM Method |
Metric Value |
English Value |
|
Melt Index @ 2300C @ 2.16 Kg |
D1238 |
1.2 g/10 min. |
|
| Specific Gravity |
D792 |
1.211 g/cc |
|
| Tensile Strength |
D638 |
21.4 MPa |
3,100 psi |
|
Elongation at Break |
D638 |
950% |
950% |
|
Flexural Modulus |
D790 |
965 MPa |
140,000 psi |
|
Flexural Strength |
D790 |
27.6 MPa |
4,000 psi |
|
Notched Izod |
D256 |
262 J/m |
5 ftlb/in |
|
Heat Deflection Temperature 66 psi |
D648 |
910C Annealed |
1950F Annealed |
|
Flammability |
ICC Laboratory Test in accordance with UL-94V Test Procedure |
V-0 @ 1.5mm |
V-0 @ 0.0625 in. |
Caution: This product contains a special FR component which may lose its effectiveness after repeated extrusions. Regrind content of blends should be kept to a minimum and the fire retardancy of resulting sheet tested prior to sale.
Note: These data are typical properties and are not to be used for establishing minimum material specifications. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Chemical Corporation for specific data to meet your design criteria.