20% TALC FILLED
POLYPROPYLENE
FARALLOY PP-259
FARALLOY PP-259 is a 20% talc filled injection moldable grade polypropylene.
| Physical Property |
ASTM Method |
Metric Value |
English Value |
|
Melt Index @ 2300C @ 2.16 Kg |
D1238 |
10 g/10 min. |
|
| Specific Gravity |
D792 |
1.04 g/cc |
|
| Tensile Strength |
D638 |
18.1 MPa |
2,630 psi |
|
Elongation at Break |
D638 |
10% |
10% |
|
Flexural Modulus |
D790 |
903 MPa |
131,000 psi |
|
Flexural Strength |
D790 |
47.5 MPa |
6,900 psi |
|
Notched Izod |
D256 |
320 J/m |
6 ftlb/in |
|
Heat Deflection Temperature 66 psi |
D648 |
850C |
1850F |
Note: These data are typical properties and are not to be used for establishing minimum material specifications. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Chemical Corporation for specific data to meet your design criteria.