FLAME RETARDANT POLYSTYRENE FARALLOYÒ PS-101 |
FARALLOY PS-101 is an extrusion grade high impact polystyrene formulated to resist ignition as defined by Underwriters' Laboratories 94V test protocol.
|
Physical Property |
ASTM Method | Metric Value | English Value |
| Melt Index @ 200° C @ 5.0 Kg | D1238 | 6.0 g/10 min. | |
| Specific Gravity | D792 | 1.15 g/cc | |
| Tensile Strength | D638 | 22.0 MPa | 3,200 psi |
| Elongation at Break | D638 | 55% | 55% |
| Flexural Modulus | D790 | 1,720 MPa | 250,000 psi |
| Flexural Strength | D790 | 53.1 MPa | 7,700 psi |
| Notched Izod | D256 | 106.7 J/m | 2.0 ft lb/in |
| Vicat Softening Temperature 66 psi | D1525 | 96° C | 205° F |
| Heat Deflection Temperature 66 psi | D648 | 77° C | 170° F |
| Flammability | UL-94V Recognized in all colors | V-0 @ 1.5mm 5VA @ 4.2mm | V-0 @ 0.0625 in. 5VA @ 0.167 in. |
NOTE: These data are typical properties and are not to be used for establishing material minimums. They are the latest available at time of publication and are authentic to the best knowledge of the company. The properties are listed solely to give general guidance and are not to be construed as a warranty of any type. Please contact ICC Chemical Corporation for specific data to meet your design criteria.